A hypothetical A-B alloy of composition 57 wt% B-43 wt% A at some temperature is found to consist of mass fractions of 0.5 for both and phases. If the composition of the phase is 87 wt% B-13 wt% A, what is the composition of the phase

Answers: 1

Show answers

Other questions on the subject: Engineering

Engineering, 03.07.2019 14:10, volleyballfun24

If the thermal strain developed in polyimide film during deposition is given as 0.0044. assume room temperature is kept at 17.3 c, and thermal coefficient of expansion for the film and the substrate are 54 x 10^-6c^-1 and 3.3 x 10^-6c^-1respectively. calculate the deposition temperature.

Answers: 3

continue

Engineering, 04.07.2019 18:10, viicborella

Steel is coated with a thin layer of ceramic to protect against corrosion. what do you expect to happen to the coating when the temperature of the steel is increased significantly? explain.

Answers: 1

continue

Engineering, 04.07.2019 18:10, Candi9697

A-mn has a cubic structure with a0 0.8931 nm and a density of 7.47 g/cm3. b-mn has a different cubic structure, with a0 0.6326 nm and a density of 7.26 g/cm3. the atomic weight of manganese is 54.938 g/mol and the atomic radius is 0.112 nm. determine the percent volume change that would occur if a-mn transforms to b-mn.

Answers: 2

continue

Engineering, 04.07.2019 18:10, oliviasoreo92

Compute the pressure drop of 30°c air flowing with a mean velocity of 8 m/s in a circular sheet-metal duct 300 mm in diameter and 15 m long. use a friction factor, f 0.02, and pair = 1.1644 kg/m a. 37.26 pa b. 25.27 pa n c. 29.34 pa d. 30.52 pa

Answers: 1

continue

Do you know the correct answer?

A hypothetical A-B alloy of composition 57 wt% B-43 wt% A at some temperature is found to consist of...