Steady-state creep data taken for an iron at a stress level of 139 mpa are given here:
'ϵs(h−1) t(k)
6.6 x 10^−48 1090.
8.8 x 10^−2 1200
if it is known that the value of the stress exponent n for this alloy is 8.4, compute the steady-state creep rate at 1310 k and a stress level of 87 mpa.

Answers: 1

Show answers

Other questions on the subject: Engineering

Engineering, 04.07.2019 16:10, TheOriginalMeyah

An electrical motor raises a 50kg load at a construct velencity .calculate the power of the motor, if it takes 40sec to raise the load through a height of 24m(take g =9.8n/g)

Answers: 2

continue

Engineering, 04.07.2019 18:10, Candi9697

A-mn has a cubic structure with a0 0.8931 nm and a density of 7.47 g/cm3. b-mn has a different cubic structure, with a0 0.6326 nm and a density of 7.26 g/cm3. the atomic weight of manganese is 54.938 g/mol and the atomic radius is 0.112 nm. determine the percent volume change that would occur if a-mn transforms to b-mn.

Answers: 2

continue

Engineering, 04.07.2019 18:10, namira16

Which of the following controllers anticipates the future from the slope of errors over time? a)-proportional b)-on/off c)-integral d)-derivative.

Answers: 2

continue

Engineering, 04.07.2019 18:20, DroctorWellsfan

Inspection for bearing condition will include: (clo4) a)-color b)-smell c)-size d)-none of the above

Answers: 1

continue

Do you know the correct answer?

Steady-state creep data taken for an iron at a stress level of 139 mpa are given here:
'ϵs(h−...