Ahypothetical metal alloy has a grain diameter of 2.4 × 10−2 mm. after a heat treatment at 575°c for 500 min, the grain diameter has increased to 5.6 × 10−2 mm. compute the time required for a specimen of this same material (i. e., d0 = 2.4 × 10−2 mm) to achieve a grain diameter of 5.5 × 10−2 mm while being heated at 575°c. assume the n grain diameter exponent has a value of 2.2.

Line joining liquid phase with liquid and solid phase mixture is known as: a) liquidus b) solidus c) tie line d) none of the mentioned

Two flowing streams of argon gas are adiabatically mixed to form a single flow/stream. one stream is 1.5 kg/s at 400 kpa and 200 c while the second stream is 2kg/s at 500 kpa and 100 ? . it is stated that the exit state of the mixed single flow of argon gas is 150 c and 300 kpa. assuming there is no work output or input during the mixing process, does this process violate either the first or the second law or both? explain and state all your assumptions.

Select any two (2) areas of applications of chain-drive. (clo4) a)-permanent lubrication necessary b)-hydraulic forklift truck operation c)-rigging and heavy moving materials d)-relatively high maintenance costs e)-costlier than belt drives