Engineering, 06.11.2019 06:31, lazavionadams81

7.43 a non-cold-worked brass specimen of average grain size 0.008 mm has a yield strength of 160 mpa (23,500 psi). estimate the yield strength of this alloy after it has been heated to 600°c for 1000 s, if it is known that the value of ky is 12.0 mpa-mm1/2 (1740 psi-mm1/2).

Answers: 2

Show answers

Other questions on the subject: Engineering

Engineering, 04.07.2019 18:10, settasav9641

Abrake has a normal braking torque of 2.8 kip in and heat-dissipating cast-iron surfaces whose mass is 40 lbm. suppose a load is brought to rest in 8.0 s from an initial angular speed of 1600 rev/min using the normal braking torque; estimate the temperature rise of the heat dissipating surfaces.

Answers: 3

continue

Engineering, 04.07.2019 18:10, johnthienann58

Thermal stresses are developed in a metal when its a) initial temperature is changed b) final temperature is changed c) density is changed d) thermal deformation is prevented e) expansion is prevented f) contraction is prevented

Answers: 2

continue

Engineering, 04.07.2019 18:20, safiyabrowne7594

Ahe-xe mixture containing a 0.75 mole fraction of helium is used for cooling electronics in an avionics application. at a temperature of 300 k and atmospheric pressure, calculate the mass fraction of helium and the mass density, molar concentration and molecular weight of the mixture. if the cooling capacity is 10 l, what is the mass of the coolant?

Answers: 3

continue

Engineering, 04.07.2019 18:20, kendrawalraven

The characteristic roots of a dynamic system are: 1.7920 1.8160 i, -1.7920 1.8160 i, -0.4160 what is the order of this system? what are the settling time and damping ratio of the system?

Answers: 3

continue

Do you know the correct answer?

7.43 a non-cold-worked brass specimen of average grain size 0.008 mm has a yield strength of 160 mpa...